This product is specially applied to Semiconductor, Crystal, Porcelain, and Magnetic material ingot/block cutting.
• Excellent adhesive strength • Quick hardening • Easy to be debonded by hot water without using solvent or oven • Easy to be blended (Weight Ratio A : B = 2 : 1) • Good for large area mounting • Non-flammability, no disgusting smell • Customization is available upon request
| GigaBond | V1 | V7 | ||||||||
| Viscosity cps (25°C)C) | A | B | A | B | ||||||
| 165000 | 42000 | 25000 | 25000 | |||||||
| ± 15000 | ± 7000 | ± 5000 | ± 5000 | |||||||
| Appearance | Rust | White | Rust | White | ||||||
| Gel Time | 3 ~ 5 (min) | 5 ~ 8 (min) | ||||||||
| Bond Strength | After 0.5 Hours | After 2 Hours | ||||||||
| 80 (kg/cm2) | 100 (kg/cm2) | |||||||||
| Max. Strength | After 1 Hours | After 6 Hours | ||||||||
| 100 (kg/cm2) | 200 (kg/cm2) | |||||||||
| Hardness | 85 ± 5D | 85 ± 5D | ||||||||
| Mixing Ratio | A : B = 1 : 1 | |||||||||
| Application | Sapphire slicing | Bonding Fixture | ||||||||
| Debonding | 70°C Water | 200°C Oven | ||||||||
| Debonding Time | 10 min | 30 min | ||||||||
| Package | A : 1KG / B：1KG | |||||||||
| GigaBond | V9 | |||||||||
| Viscosity cps (25°C) | A | B | ||||||||
| 150000 | 50000 | |||||||||
| ± 15000 | ± 10000 | |||||||||
| Appearance | Rust | White | ||||||||
| Gel Time | 3 ~ 7 (min) | |||||||||
| Bond Strength | After 2 Hours | |||||||||
| 100 (kg/cm2) | ||||||||||
| Max. Strength | After 4 Hours | |||||||||
| 150 (kg/cm2) | ||||||||||
| Hardness | 85 ± 5D | |||||||||
| Mixing Ratio | A : B = 1 : 1 | |||||||||
| Application | Sapphire slicing | Bonding Fixture | ||||||||
| Debonding | 70°C Water | 200°C Oven | ||||||||
| Debonding Time | 20 min | 30 min | ||||||||
| Package | A : 1KG / B：1KG | |||||||||
| GigaBond | S4 | S7 | ||||||||
| Viscosity cps (25°C) | A | B | A | B | ||||||
| 70000 | 16000 | 20000 | 3000 | |||||||
| ± 10000 | ± 5000 | ± 5000 | ± 1000 | |||||||
| Appearance | Rust | Milky | Rust | Milky | ||||||
| Gel Time | 20 (min) | 10 (min) | ||||||||
| Bond Strength | After 2 Hours | After 2 Hours | ||||||||
| 200 (kg/cm2) | 200 (kg/cm2) | |||||||||
| Max. Strength | After 6 Hours | After 6 Hours | ||||||||
| 240 (kg/cm2) | 240 (kg/cm2) | |||||||||
| Hardness | 85 ± 5D | 85 ± 5D | ||||||||
| Mixing Ratio | A : B = 2 : 1 | |||||||||
| Application | Silicon Slicing | |||||||||
| Debonding | 75°C Water | |||||||||
| Debonding Time | 15 min | |||||||||
| Package | A : 1KG / B：0.5KG | |||||||||